Electrospun Fibers from Polysaccharides

Abstract

Although chitin has limited solubility in common solvents, chitin and chitin derivatives have been electrospun into fibers for various applications. To produce electrospun fibers, chitin was first depolymerized using irradiation and then dissolved using 1,1,1,3,3,3-hexafluoro 2-propanol and fibers with average diameters of 110 nm were obtained [04Min]. After electrospinning, the chitin mats were deacetylated using 40 % aqueous NaOH solution at 60–100 °C to achieve about 85 % deacetylation and form chitosan fibers. SEM images and some of the properties of the chitin and chitosan fibers obtained after deacetylation of the spun chitin membranes are shown in Fig. 58.1. Minimal changes were observed in the diameters of the fibers before and after deacetylation.

Cite this page

References (68)

About this content

Title
Electrospun Fibers from Polysaccharides
Book Title
Innovative Biofibers from Renewable Resources
In
Electrospun Fibers from Biopolymers
Book DOI
10.1007/978-3-662-45136-6
Chapter DOI
10.1007/978-3-662-45136-6_58
Part of
Volume
Editors
Authors
  • Narendra Reddy (3)
  • Yiqi Yang (4)
  • Author Affiliation
  • 3 Centre for Emerging Technologies, Jain University, Bangalore, India
  • 4 Department of Textiles, Merchandising and Fashion Design, University of Nebraska-Lincoln, Lincoln, NE, USA
  • Cite this content

    Citation copied