Biocomposites Developed Using Protein-Based Materials as Matrix

Abstract

Unlike the familiar approach of using natural fibers or agricultural residues as reinforcement and synthetic polymers as matrix, attempts have been made to use matrix from renewable resources with various types of reinforcement [13Mon]. In one such attempt, wheat gluten was used as the matrix and wheat straw ground to various lengths was used as reinforcement. Wheat straw lengths obtained were 2 mm, 0.2 mm, and less than 0.2 μm. The ground wheat straw was mixed with wheat gluten with the addition of glycerol (30 %) as plasticizer, and the mixture was compression molded at 120 °C for 5 min. Some of the properties of the composites obtained are given in Table 69.1. As seen from the table, increasing the fiber content increased the strength and modulus but decreased the elongation. Similarly, impact- and ball-milled fibers provided better tensile properties than the cut-milled fibers at similar levels of fiber loading [13Mon]. Although composites made using wheat gluten and wheat straws have good tensile properties, the wheat gluten and plasticizer are highly hydrophilic and absorb considerable amounts of water. Such composites are expected to have poor stability at high humidities or under aqueous environments and therefore not useful for practical applications.

Cite this page

References (14)

About this content

Title
Biocomposites Developed Using Protein-Based Materials as Matrix
Book Title
Innovative Biofibers from Renewable Resources
In
Biocomposites from Renewable Resources
Book DOI
10.1007/978-3-662-45136-6
Chapter DOI
10.1007/978-3-662-45136-6_69
Part of
Volume
Editors
Authors
  • Narendra Reddy (3)
  • Yiqi Yang (4)
  • Author Affiliation
  • 3 Centre for Emerging Technologies, Jain University, Bangalore, India
  • 4 Department of Textiles, Merchandising and Fashion Design, University of Nebraska-Lincoln, Lincoln, NE, USA
  • Cite this content

    Citation copied